Akira, Muhammad Wira and Haritsah, Hanuna and Zulfia, Anne and Prajatelistia, Ekavianti (2021) Mechanical and tribological properties of nano-sized Al2O3 particles on ADC12 alloy composites with Strontium modifier produced by stir casting method. ADI Journal on Recent Innovation (AJRI), 3 (1). pp. 1-12. ISSN 2686-0384
Text
2-v3n1-2021.pdf - Published Version Restricted to Registered users only Download (2MB) |
Abstract
Nano-Al2O3 particles were incorporated into ADC12 alloy with the addition of Al-5Ti-B, Al-Sr, and Mg to achieve high performance in mechanical and tribological properties. In this study, varied nano-Al2O3 was used from 0.25 vf-% to 0.5 vf-% through stir casting methods to discover the optimum amount to obtain high performance. Besides, the inclusion of grain refiner Al-5Ti-B and microstructure modifier Al-Sr is expected to improve performance to the next level. However, porosity and agglomeration still be a concern in Aluminum alloy matrix composite fabrication. The presence of spinel phase MgAl2O4 in the interface area between nano-Al2O3 particles and ADC12 alloy is relied upon to minimize this porosity and agglomeration issue. The optimum of tensile strength and hardness was found at 0.35 vf-% Al2O3 and wear rate at 0.4 vf%. Although, the optimum point of wear found at 0.4 vf%, porosity began to increase at 0.4 vf% as well. As a result, 0.35 vf% addition of the nano-Al2O3 gives the best performance for the composite.
Item Type: | Article |
---|---|
Subjects: | General > ADC12 Alloy General > Particles |
Depositing User: | Admin Digital Blue Ocean |
Date Deposited: | 11 Jul 2023 16:26 |
Last Modified: | 11 Jul 2023 16:26 |
URI: | http://dbo.raharja.ac.id/id/eprint/1635 |
Actions (login required)
View Item |